Wurth Liquid Metal FE 1 (500gm)

• High-quality two-component reaction resin system that exhibits characteristics similar to those of metal due to its special formula
• The ideal mixing ratio of the components (A:B = 1:1, pressing out two strands of the same length from the tubes) makes incorrect mixing of the repair compound virtually impossible
• Specifically designed for smaller repair jobs where a quick turnaround is required
• Can be applied with a spatula and does not run, which also makes vertical application possible
• After hardening, Liquid Metal Fe1 can easily be processed in the same way as metal with lathing, milling, drilling, filing or thread cutting

Technical information

• Mixing ratio: Component A: Component B = 1:1
• Density: 2.8 kg/m³
• Density conditions: Components A and B mixed
• Colour: Grey
• Min./max. gelation time: 7-12 min
• Min./max. curing time: 4-24 h
• Fully hardening/curing conditions: Room temperature
• Conditions for gelation time: at room temperature
• Working life: 5 min
• Conditions for working life: at 20°C, 20 g total mass
• Viscosity/consistency: Pasty
• Min. tensile strength: 12.5 N/mm²
• Min. combined tension and shear resistance: 14.5 N/mm²
• Coefficient of thermal expansion: 0.0004 1/K
• Min. compressive strength: 70 N/mm²
• Min./max. temperature resistance of the hardened material: -60 to 120 °C
• Weight of content: 500 g